Vol.59, No.4, 273 ~ 281, 2021
|
| Title |
| Characterization of the Strength of a Natural Sand and Artificial Sand Core Manufactured with Inorganic Binder |
| 배민아 Min A Bae , 김판성 Pan Seong Kim , 김경호 Kyeong Ho Kim , 이만식 Man Sig Lee , 백재호 Jae Ho Baek |
|
|
|
| Abstract |
| Natural sand and organic binders are commonly used in casting processes, but these ingredients produce environmental problems with dust and harmful TVOC(Total Volatile Organic Carbon) gases. Research on the introduction of artificial sand and inorganic binders to solve these environmental problems is being actively conducted mainly in the casting industry. Artificial sand has superior durability and a spherical shape compared to natural sand, and above all, it does not generate dust. In addition, inorganic binders have the advantage that no harmful gas is generated during casting and the used sand can be recycled. This study confirmed whether inorganic binders can be applied when replacing natural sand with artificial sand. First, eco-friendly inorganic binders that do not produce harmful gas were synthesized. Then characteristic analyses were carried out with artificial sand and natural sand. Physical and chemical properties were compared using X-Ray Fluorescence (XRF), Powder Flow Test (PFT) and particle size distribution analyses. The general strength and absorption (absolute humidity 29.9 g/cm3) strength of the sample core was measured using each sand (artificial sand, natural sand) and inorganic binder. Also, X-ray Photoelectron Spectroscope (XPS) analysis confirmed the combination structure. As a result, it was confirmed that artificial sand exhibited mold characteristics with similar strength even with lower inorganic binder content than natural sand.
(Received January 5, 2021; Accepted February 8, 2021) |
|
|
| Key Words |
| inorganic binder, sand core, natural sand, artificial sand, strength |
|
|
 |
|