Vol.58, No.4, 263 ~ 272, 2020
|
| Title |
| Effects of Growth Temperature on the Physicochemical and Photoelectrochemical Properties of a Modified Chemical Bath Deposited Fe2O3 Photoelectrode |
| 홍예진 Yaejin Hong , 전승환 Seung-hwan Jeon , 류혁현 Hyukhyun Ryu , 이원재 Won-jae Lee |
|
|
|
| Abstract |
| In this study, Fe2O3 photoelectrode thin films were grown on fluorine-doped tin oxide substrates at various temperatures ranging from 145 to 220 ℃ using modified chemical bath deposition. The morphological, structural, electrical, and photoelectrochemical properties of the resulting Fe2O3 photoelectrode were analyzed using field emission scanning electron microscopy, X-ray diffraction, electrochemical impedance spectroscopy, and a three-electrode potentiostat/galvanostat, respectively. Growth temperature and hydrochloric acid etching both affected the growth of the Fe2O3 photoelectrode, with Fe2O3 thin film thickness first increasing and then decreasing as growth temperature increased. The pH value of the precursor solution varied according to growth temperature, which in turn affected film thickness. The highest photocurrent density (0.53 mA/cm2 at 0.5 V vs. saturated calomel electrode) was obtained from the Fe2O3 photoelectrode grown at 190 ℃, which yielded the thickest thin film, smallest full width at half maximum and largest grain size for the (104) and (110) plane, and highest flat-band potential value. Based on these findings, the photoelectrochemical properties of Fe2O3 photoelectrodes grown at various temperatures are strongly affected by their morphological, structural, and electrical properties.
(Received August 12, 2019; Accepted December 11, 2019) |
|
|
| Key Words |
| Fe2O3, modified chemical bath deposition (M-CBD), growth temperature, HCl etching, photoelectrochemical (PEC) |
|
|
 |
|