Vol.56, No.1, 49 ~ 59, 2018
|
| Title |
| Recovery of Fine Aluminum Hydroxide with High Whiteness Index from Low Quality Bauxite Using Caustic Roasting and Water Leaching |
| Su Jin Kim , Jeong Il Lee , Kyu Sung Han , So Yeong Byun , Tam Tran , Myong Jun Kim |
|
|
|
| Abstract |
| A bauxite of low quality containing 6.75% reactive silica and 37.4% Al2O3 as gibbsite was roasted with additives including NaOH (caustic/total alumina molar ratio of 2-4:1) and CaO (CaO/total SiO2 molar ratio of 0.5-3:1) at 300-1000 ℃, producing calcines containing sodium aluminate (Na2O.Al2O3), silicates and hematite. Optimum conditions included roasting at 350-400 ℃ with CaO added at a CaO/total SiO2 molar ratio of 1:1 for 2-3 h. Dissolving the calcine in water at 90 ℃ produced a sodium aluminate liquor from which aluminum hydroxide (Al2O3.3H2O - alumina trihydrate or ATH) was precipitated. The addition of CaO reduced the silica extraction to <15% at optimum conditions, whereas the total organic carbon(TOC) was ~200 mg/L as carbon in all cases. Losses of alumina and caustic were experienced, as different phases of Al-Ca-Si or Na-Ca-Al-Si minerals were formed during roasting and/or leaching. The extracted alumina in the leached solution were precipitated at 60 ℃ for 20 h to produce a fine aluminum hydroxide having D50 of 1.9-2.8 μm with a whiteness index of 96.8-97.5, better than commercially available products.
(Received May 11, 2017; Accepted September 29, 2017) |
|
|
| Key Words |
| fine aluminium hydroxide, high silica, bauxite, caustic roasting, high whiteness |
|
|
 |
|