| Abstract |
| To investigate the effect of tungsten substitution of molybdenum on the formation of the second phase in Super Duplex Stainless Steel Weldments, welding wires with a composition of 3 wt% Mo, 2.2 wt% Mo-2.2 wt% W were designed for the flux cored arc welding process. As a result, the precipitation of the χ phase and σ phase increased in proportion to the decrease in the amount of δ ferrite content because the reaction, δ ferrite → σ + γ2, proceeded as the temperature rose. Under the same experimental conditions, the precipitation of the second phase, which degrades the properties of the material, was significantly reduced in the W substitution specimens compared to the Mo-only specimens. A polarization test conducted in a salt solution revealed that the pitting potential of the W substitution specimens was higher than that of the Mo-only specimens. |
|
|
| Key Words |
| metals, welding, precipitation, electron backscattering diffraction(EBSD), super duplex stainless steel |
|
|
 |
|