Vol.48, No.8, 741 ~ 749, 2010
Title
Analysis of the Effects of Ti, Si, and Mo on the Resistance to Corrosion and Oxidation of Fe-18Cr Stainless Steels by Response Surface Methodology
장희진 Hee Jin Jang , 윤귀섭 Kwi Sub Yun , 박찬진 Chan Jin Park
Abstract
We studied the corrosion and oxidation properties of Fe-18Cr-0.4Nb-(0.1~0.6)Ti-(1~3)Si-(0.5~2)Mo stainless steel. The resistance to general and pitting corrosion was evaluated and the results were analyzed by Response Surface Methodology (RSM) as a function of alloy composition. The effects of alloy composition and heat treatment on the oxidation resistance were also examined. Mo increased both general corrosion resistance and pitting corrosion resistance. Si improved the resistance of the alloys to pitting corrosion. Si was also beneficial for general corrosion resistance of the alloys containing Mo at more than 1 wt.%. However, Mo was detrimental when its content was lower. Effects of Ti on general corrosion properties appeared to be weak and a high concentration of Ti appeared to deteriorate pitting resistance. The thickness of the oxidation scale increased and adhesion of the scale worsened as the temperature increased from 800℃ to 900℃. Weight gain of the alloys due to oxidation at 900℃ clearly showed that the resistance to oxidation is improved by annealing at 860℃ and an increase of Si content.
Key Words
alloys, annealing, corrosion, oxidation, Response Surface Methodology
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.