Vol.37, No.11, 1343 ~ 1350, 1999
Title
Research Paper / Solidification : Control of Lamellar Orientation in TiAl Alloys by Directional Solidification Using a Seed Material
이호년Ho Nyun Lee,오명훈Myung Hoon Oh,D . R . Johnson,건청행Haruyuki Inui,산구정치Masaharu Yamaguchi,위당문Dang Moon Wee
Abstract
The thermal stability of the lamellar microstructure and the orientation control of the lamellar microstructure in a cast TiAl alloys with Mo and C were investigated. The lamellar stability of the seed material up to the melting temperature is important in the orientation control of the lamellar microstructure by the directional solidification. First, the partial liquidus surface was constructed for TiAl-C ternary and TiAl-1.5Mo-C quaternary systems. The lamellar stability was determined by quickly heating specimens to a temperature just below the melting temperature, holding, and then cooling to room temperature. Ti-46Al-1.5Mo-0.2C alloy was found to be a promising composition as a seed materials and ingots with a lamellar microstructure aligned along the growth direction were successfully grown by directional solidification process using the seed alloy. From the result of tensile and compression tests, directionally solidified Ti-46Al-1.5Mo-0.2C (at.%) ingots were found to exhibit a high yield stress together with a reasonably good tensile elongation at room temperature and a high compression stress up to 1000℃.
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.