Vol.46, No.6, 357 ~ 363, 2008
Title
Effects of Processing Time and Temperature on the Surface Properties of AISI 316L Stainless steel During Low Temperature Plasma itriding After Low Temperature Plasma Carburizing
이인섭 In Sup Lee
Abstract
The 2-step low temperature plasma processes (the combined carburizing and post-nitriding) were carried out for improving both the surface hardness and corrosion resistance of AISI 316L stainless steel. The effects of processing time and temperature on the surface properties during nitriding step were investigated. The expanded austenite (γN) was formed on all of the treated surface. The thickness of γN was increased up to about 20 ?m and the thickness of entire hardened layer was determined to be about 40 ?m. The surface hardness reached up to 1,200 HV0.1 which is about 5 times higher than that of untreated sample (250 HV0.1). The thickness of γN and concentration of N on the surface were increased with increasing processing time and temperature. The corrosion resistance in 2-step low temperature plasma processed austenitic stainless steels was enhanced more than that in the untreated austenitic stainless steels due to a high concentration of Non the surface.
Key Words
austenitic stainless steel, Low temperature plasma carburizing, Low temperature plasma nitriding, expanded austenite
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.