Vol.40, No.7, 811 ~ 818, 2002
Title
Research Papers / Physical Chemistry : Effect of Al2O3 , SiO2 and MgO on the Formation of Calcium Ferrites in Sinter using X-ray Diffraction Method
박준현Jun Hyun Park,조유정Yu Jeong Cho,윤성섭Sung Seop Yoon,김형순Hyung Sun Kim,허완욱Wan Wook Huh
Abstract
In order to elucidate the fundamental aspects of the minerals formation processes during sintering, the Fe_2O_3-CaO-Al_2O_3-SiO_2 system and the effect of MgO on synthesized iron ore sinter were studied by image analysis and X-ray diffraction method. Most existed calcium ferrite was identified to be a solid solution of CaO·2Fe_2O_3 with a small amount of solubility of Al_2O_3 and SiO_2. With an increase of the content of Al_2O_3 in the system, the amount of calcium ferrite was increased. On the other hand, the amount of calcium ferrite was decreased, and the amount of hematite was increased with increasing the content of SiO_2. Crystal structure of calcium ferrite with Al_2O_3 and SiO_2 was changed from monoclinic to triclinic as well as the unit cell volume shrank with fixing Al_2O_3 and increasing SiO_2. With increasing the content of MgO(1∼3 wt%), the amount of magnetite was increased and hematite was decreased but calcium ferrite was not changed.
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.