Title
Research Paper - Composite Materials - : Fabrication of Ni - coated Al2O3 / Al Matrix Composites by Oxide Dispersion Strengthening
양태성T . S . Yang, 강복석B . S . Kang, 서영식Y . S . Seo, 원창환C . W . Won, 최진일J . I . Choi
Abstract
The experimental results from the fabrication of AC4C/Ni-coated Al₂O₃ composites by oxide dispersion strengthening are summerized as follows; 1) Optimum condition obtained in Ni-Al₂O₃ composites powder preparation was molar ratio of NH₃/Ni^(++) 1.5 : 1, reduction temperature 130℃, stirring speed 600rpm, hydrogen partial pressure 350 psi and reduction time 60 mins. 2) Ni coating to Al₂O₃ surface improved wettability by decreasing surface tension of the matrix and particles. 3) The tensile strength, hardness and wear resistance increased with increasing the volume fraction and decreasing the particle size. In case of the tensile strength at 12vol.% was about 25% higher than that of matrix alloy(Al-2Cu-2Mg).
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.