Study on MgO Solubility Content in CaO - SiO2 - FetO - MnO ( 〉8wt% ) - MgO - P2O5 Slag in contact with Molten Iron and its Application
박종민Jong Min Park, 손재웅Jae Woong Son, 조만형Man Hyung Dzo
Abstract
The MgO solubility is measured in the CaO-SiO₂- Fe_tO-MnO($gt;8wt%)-MgO-P₂O_5 slag system which is in equilibrium with molten iron in the temperature range of 1550˚C. The Effect of MnO on the MgO solubility and the method for calculating the MgO solubility using slag composition and temperature and discussed, respectively. The amount of MnO content itself has an effect to raise the same amount of Fe_tO content in basic slag. On the other hand, in acidic slag MnO has an effect to raise basicity. Moreover, above results are applied to real low slag operation of 250ton LD converter to study the relationship between MgO solubility and the erosion of MgO-C refractory. The MgO solubility is in the range of 5 to 5.5 wt% at blow end of low slag operation.
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.