Title
이채우 , 윤덕용
Abstract
The effects of green density and sintering time on various properties of sintered Fe-20% Cu with and without graphite addition were investigated. Sintering was carried out at 1140℃ in hydrogen atmosphere. The specimens were cylindrical ring shape and dimensional changes in O. D. and I. D. after compacting and sintering were carefully measured and compared. Fe-20% Cu compacts showed rapid growth during first 10 minutes of sintering with subsequent densification. The samples with higher green density showed larger dimensional growth and smaller shrinkage during the initial and subsequent stages of sintering. Observations of the microstructures indicate that the results can be best explained by the penetration of the iron particle boundaries by liquid copper at the beginning of the sintering process. Addition of graphitereduces the growth but has little effect on the shinkage. The effects of green density and sintering time on and degree of oil impregnation and radial crushing strength wera also investigated. The results closely follow general expectations. With increased sintering time the amount of open porosity decreased while the closed porosity did not show much change.
Key Words
| PDF
대한금속∙재료학회 │ (06633) 서울시 서초구 서초대로 56길 38 대한금속∙재료학회 회관 (서초1동 1666-12번지)
Tel : 070-4266-1646 │ FAX : 02-557-1080 │ E-mail : metal@kim.or.kr
Copyright ⓒ 2013 사단법인 대한금속∙재료학회 All rights reserved.